P. Górak,
B. Rewera
Volume 565: Issue 9
Pages 58-60
Accepted for publication: 28.05.2019 r.
The article presents the results of laboratory and field tests of road concrete with exposed photoluminescent aggregate. The scope of the research program included selection of aggregates with appropriate parameters of "cold light", selection of surface deactivator allowing optimal exposure of the aggregate. After the laboratory tests, a test section of the road concrete with exposed aggregate was made, subjected to a long-term observation and for which mechanical strength and durability tests were carried out. "Shining concrete" allows you to ensure safety by increasing the visibility of the road without having to provide lighting. From the point of view of ecology and landscape architecture not contaminated with artificial light, it can be a future-proof solution for this type of application. The tests carried out and the results obtained confirmed the durability of this type of surface exploited in our climatic conditions.
Keywords: concrete; pavement; photoluminescent aggregate; durability; aggregate exposed.
Keywords: concrete; pavement; photoluminescent aggregate; durability; aggregate exposed.
[1] Bulina Maria, Dmitry Chudakov i inni. 2006. „Agenetically encoded photosensitizer”. Nat Biotechnol 24 (1): 95-9. /pmid: 16369538.
[2] Jabłoński Aleksander. 1933. „Effiiency of AntiStokes Fluorescence in Dyes”. Nature, vol. 131.
[3] PKN-CEN/TS 12390-9:2017-07 Badania betonu – Część 9: Oznaczanie odporności na zamrażanie i rozmrażanie w obecności soli odladzających – Złuszczanie.
[4] Pluciński Tomasz. 1997. Doświadczenia chemiczne. Warszawa. Wydawnictwo Adamantan. [5] PN-B-06265 Krajowe uzupełnienie normy PN-EN 206:2016-12 Beton.Wymagania, właściwości, produkcja i zgodność.
[6] PN-EN 12350-2:2011 Badania mieszanki betonowej – Część 2: Badanie konsystencji metodą opadu stożka.
[7] PN-EN 12350-7:2011 Badania mieszanki betonowej – Część 7: Badanie zawartości powietrza – Metody ciśnieniowe.
[8] PN-EN12390-3:2011Badania betonu – Część 3: Wytrzymałość na ściskanie próbek do badań.
[9] PN-EN 12390-6:2011 Badania betonu – Część 6: Wytrzymałość na rozciąganie przy rozłupywaniu próbek do badań.
[10] PN-EN 206+A1:2016-12 Beton – Wymagania, właściwości, produkcja i zgodność.
[11] Przibram Karl. 1935. „Fluorescence of Fluorite and the Bivalent Europium Ion”. Nature: 135.
[12] Rizzuto R. Philipp, BriniMarisa i inni. 1995. „Chimeric green fluorescent protein as a tool for visualizing subcellular organelles in living cells”. Curr Biol. 5 (6): 635-42./pmid:7552174.
[2] Jabłoński Aleksander. 1933. „Effiiency of AntiStokes Fluorescence in Dyes”. Nature, vol. 131.
[3] PKN-CEN/TS 12390-9:2017-07 Badania betonu – Część 9: Oznaczanie odporności na zamrażanie i rozmrażanie w obecności soli odladzających – Złuszczanie.
[4] Pluciński Tomasz. 1997. Doświadczenia chemiczne. Warszawa. Wydawnictwo Adamantan. [5] PN-B-06265 Krajowe uzupełnienie normy PN-EN 206:2016-12 Beton.Wymagania, właściwości, produkcja i zgodność.
[6] PN-EN 12350-2:2011 Badania mieszanki betonowej – Część 2: Badanie konsystencji metodą opadu stożka.
[7] PN-EN 12350-7:2011 Badania mieszanki betonowej – Część 7: Badanie zawartości powietrza – Metody ciśnieniowe.
[8] PN-EN12390-3:2011Badania betonu – Część 3: Wytrzymałość na ściskanie próbek do badań.
[9] PN-EN 12390-6:2011 Badania betonu – Część 6: Wytrzymałość na rozciąganie przy rozłupywaniu próbek do badań.
[10] PN-EN 206+A1:2016-12 Beton – Wymagania, właściwości, produkcja i zgodność.
[11] Przibram Karl. 1935. „Fluorescence of Fluorite and the Bivalent Europium Ion”. Nature: 135.
[12] Rizzuto R. Philipp, BriniMarisa i inni. 1995. „Chimeric green fluorescent protein as a tool for visualizing subcellular organelles in living cells”. Curr Biol. 5 (6): 635-42./pmid:7552174.
mgr inż. Piotr Górak, CEMEX Polska Sp. z o.o.
ORCID: 0000-0003-3479-7647
mgr inż. Bartosz Rewera, CEMEX Polska Sp. z o.o.
ORCID: 0000-0003-3479-7647
mgr inż. Bartosz Rewera, CEMEX Polska Sp. z o.o.
mgr inż. Piotr Górak
Full paper: