Effect of the addition of polypropylene fibers to the bonding agent on pull-off strength of coating made of epoxy resin


Vol. 579 (11) 2020 / wtorek, 24 listopada, 2020


(InPolish)

Kampa Łukasz, Sadowski Łukasz. 2020. Effect of the addition of polypropylene fibers to the bonding agent on pull-off strength of coating made of epoxy resin. Volume 579. Issue 11. Pages 40-41. DOI: 10.15199/33.2020.11.04

Accepted for publication: 29.10 2020

The article presents an analysis of the addition of polypropylene fibers to the bonding agent on the pull-off strength of coating made of epoxy resin. The fibers were added to the bonding agent in an amount of 0.5%, 1%, 1.5%and 2%in relation to mass of the epoxy resin. The modified bonding agent was laid on substratemade of cementmortar and then the coating was laid. The obtained results were confirmed with the reference coating – without the addition of polypropylene fibers to the bonding agent. Based on the obtained results the increase of the pull-off strength of coatin made with the addition of 0.5 and 1% of polypropylene fibers to the bonding agent in relation the the reference coating.
  1. Ahn N. 2003. „Effects of diacrylatemonomers on the bond strength of polymer concrete to wet substrates”. J. Appl. Polym. Sci. 90, 991–1000.
  2. Chowaniec A., Łukasz Sadowski, A. Żak. 2020. „The chemical and microstructural analysis of the adhesive properties of epoxy resin coatings modified using waste glass powder”. Appl. Surf. Sci. 504, 144373.
  3. Do J., Y. Soh. 2003. „Performance of polymer- modified self-leveling mortars with high polymer– cement ratio for floor finishing”. Cem. Concr. Res. 33, 1497 – 1505.
  4. Dutra R. C., B. G. Soares, E.A. Campos, J. D. DeMelo, J. L. Silva. 1999. „Composite materials constituted by amodified polypropylene fiber and epoxy resin”. J. Appl. Polym. Sci. 73, 69 –73.
  5. HaoY., F. Liu, H. Shi, E. Han, Z.Wang. 2011. „The influence of ultra-fine glass fibers on the mechanical and anticorrosion properties of epoxy coatings”. Prog. Org. Coat. 71, 188 – 197.
  6. Horgnies M.; P. Willieme, O. Gabet. 2011. „Influence of the surface properties of concrete on the adhesion of coating: Characterization of the interface by peel test and FT-IR spectroscopy”. Prog. Org. Coat. 72, 360 – 379.
  7. Kampa Łukasz, Łukasz Sadowski. Środek gruntujący do wykonywania posadzek epoksydowych oraz sposób jego otrzymywania. Zgłoszenie patentowe nr P. 435371.
  8. Krzywiński K., Łukasz Sadowski. 2019. „The effect of texturing of the surface of concrete substrate on the pull-off strength of epoxy resin coating”. Coatings 9, 143.
  9. Pourhashema S., M. Vaezia, A. Rashidib. 2017. „Investigating the effect of SiO2 – graphene oxide hybrid as inorganic nanofiller on corrosion protection properties of epoxy coatings”. Surf. Coat. Technol. 311, 282 – 294.
  10. Sadowski Łukasz; S. Czarnecki, J. Hoła. 2016. „Evaluation of the height 3D roughness parameters of concrete substrate and the adhesion to epoxy resin”. Inter. J. Adhes. Adhes 67, 3 – 4.
  11. Szymanowski J. 2019. „Evaluation of the adhesion between overlays and substrates in concrete floors: Literature survey, recent non-destructive and semi-destructive testing methods, and research gaps”. Buildings 9, 203.
techn. Łukasz Kampa, Politechnika Wrocławska; Wydział Budownictwa Lądowego i Wodnego ORCID: 0000-0003-0884-8076
dr hab. inż. Łukasz Sadowski, prof. uczelni, Politechnika Wrocławska; Wydział Budownictwa Lądowego i Wodnego ORCID: 0000-0001-9382-7709

techn. Łukasz Kampa, Politechnika Wrocławska; Wydział Budownictwa Lądowego i Wodnego ORCID: 0000-0003-0884-8076

 lukasz.kampa@pwr.edu.pl

Full paper is available at Publisher house SIGMA-NOT Sp. z o.o. webpage

DOI: 10.15199/33.2020.11.04