Properties of concrete containing calcium sulphoaluminate cement (CSA)

Vol. 554 (10) 2018 / poniedziałek, 22 października, 2018

(in Polish)

M. Batog,
K. Synowiec,
D. Dziuk,
I. M. Maurizio

DOI:10.15199/33.2018.10.01

Volume 554:
Issue 10
Pages 5-8

In the herby paper the properties of calcium sulphoaluminate cement CSAand its impact on the properties of fresh and hardened concrete are explored. Application of CSA cement as a component of concrete allows to achieve very high early strengths, even 25 MPa after 6,5 hours of hardening. Key aspect in the practical application of CSA cement in concrete is the control of setting time of concrete mix by the use proper retarding admixtures. The composites prepared in this experimentation containing CSAcement have shown comparable durability to those made of Portland cement. They are characterized by very good frost resistance (without and in the presence of de-icing agents), as well as low permeability of chloride ions and low carbonation depth. Keywords: calcium sulphoaluminate clinker; repair concrete; durability; freeze-thaw resistance.
  • [1] Bye Gerry C. 2009. Portland cement: Composition, production and properties. London: Thomas Telford Ltd.
  • [2] Deklaracja środowiskowa dla cementu glinowego Cimsa ISIDAC 40, nr rej. EPD-CIS-20150242 CAA1-EN z 3.11.2015. Institut Bauen und Umwelt e.V. (IBU). http://ibu-epd.com/.
  • [3] Deklaracja środowiskowa dla produktów i.techAli Pre Green i i.techAli CemGreen, nr rej.MR ENV-EPD-ICG-20160002-EN z 23.12.2015. Institut Bauen und Umwelt e.V. (IBU). http://ibu-epd.com/.
  • [4] Deklaracja środowiskowa dla cementu CEMI 52,5R, nr rej. EPD-HCG- 20160145-CAD1-EN z 10.11.2016. Institut Bauen und Umwelt e.V. (IBU). http://ibu-epd.com/.
  • [5] HeidelbergCement Group. 2010 ÷ 2018. Materiały wewnętrzene.
  • [6] https://www.concretum.com/references/.
  • [7] Juenger Maria, Frank Winnefeld, John Provis, Jason Ideker. 2011. „Advances in Alternative Cementitious Binders”. Cement and Concrete Research 41 (12): 1232–43. https://doi.org/10.1016/j.cemconres.2010.11.012.
  • [8] KurdowskiWieslaw. 2010. Chemia cementu i betonu. Kraków,Warszawa: Stowarzyszenie Producentów Cementu,Wydawnictwo Naukowe PWN.
  • [9] Nocuń-Wczelik Wiesława, Zofia Konik, Andrzej Stok, Jan Małolepszy. 2003. „Spoiwa o kontrolowanych zmianach objętości do prac naprawczych i uszczelniających”. Przegląd Budowlany 12: 32 – 36.
  • [10] Lee Keon-Ho, Nam Seong-Young, Min Seung-Eui, Lee Hyoung-Woo, Han Choon, Ahn Ji Whan. 2016. „Characterizations of high early-strength type shrinkage reducing cement and calcium sulfo-aluminate by using industrial wastes”. Journal of the Korean Ceramic Society 53 (2): 215 – 21.
  • [11] MarchiMaurcio,Umberto Costa. 2011. Influence of the calciumsulphate and w/c-ratio on the hydration of calciumsulfoaluminate cement. Materiały konferencyjne z XIII Międzynarodowego Kongresu Chemii Cementu.
  • [12] Odler Ivan. 2000. Special inorganic cements. NewYork: E & FN Spon.
  • [13] PN-EN 13877-2:2013-08 Nawierzchnie betonowe – Część 2: Wymagania funkcjonalne dla nawierzchni betonowych.
  • [14] PN-EN 196-9:2010Metody badania cementu – Część 9: Ciepło hydratacji – metoda semiadiabatyczna.
  • [15] PN-EN 206+A1:2016-12 Beton –Wymagania, właściwości, produkcja i zgodność.
  • [16] Popescu Constantin Dorel, Marcela Muntean, John Sharp. 2003. „Industrial trial production of lowenergy belite cement”. Cement and Concrete Composites 25 (7): 689–93. https://doi.org/10.1016/S0958-9465 (02) 00097-5.
dr inż. Maciej Batog

Full paper is available at Publisher house SIGMA-NOT Sp. z o.o. webpage

DOI: 10.15199/33.2018.10.01